ECCOBOND UV 3000
Harmonization Code : 3919.10.80 | Other self-adhesive plastic rolls not exceeding 20 cm wide.
Main features
- UV-Curable Epoxy Chemistry
- High-Temperature Performance
- Low Outgassing and Chemical Resistance
Product Description
LOCTITE ECCOBOND UV 3000 is a clear, UV-curable epoxy adhesive designed for high-throughput assembly operations. The material cures through ultraviolet light using a cationic cure mechanism and is commonly used for glass bonding and optoelectronic lens attachment applications. With a medium viscosity of approximately 5,300 cP, low outgassing characteristics, chemical resistance, and thermal stability at temperatures up to 200°C, it can support demanding bonding applications where optical clarity, environmental resistance, and elevated-temperature performance are important considerations.
Key features
- UV-curable epoxy chemistry: Supports rapid processing using UV exposure for high-throughput manufacturing environments.
- High-temperature performance: Can withstand exposure to temperatures as high as 200°C.
- Low outgassing and chemical resistance: Suitable for applications where contamination control and environmental durability are important.
Applications / Suitable for
- Glass bonding
- Lens attachment
- Optoelectronic assemblies
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
Typical as-supplied properties and handling information.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Clear | — | As supplied |
| Viscosity | 5,300 | mPa·s (cP) | Brookfield HBT, Spindle 7, 10 rpm, 25°C |
| Specific Gravity | 1.09 | — | 25°C |
| Shelf Life | 365 | days | From date of manufacture |
| Recommended UV Intensity | 200 | mW/cm² | UV curing guideline |
After-processing / final-state properties
Typical properties after UV cure.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Glass Transition Temperature (Tg) | 150 | °C | Cured material |
| Coefficient of Thermal Expansion (Alpha 1) | 75 | ppm | 40–120°C |
| Chloride Ion Content | <10 | ppm | 121°C extraction |
| Sodium Ion Content | <5 | ppm | 121°C extraction |
| Potassium Ion Content | <5 | ppm | 121°C extraction |