LOCTITE PC9410
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- 3 to 11 Minute Initial Set
- -25 to 45 deg C Placement Range
- 17 to 21 N/mm^2 Strength After 2 Hours
Product Description
LOCTITE PC 9410 is a two-component magnesium phosphate-based system for concrete repair and grouting in potholes, loading areas, anchoring, and machinery-support work. Aggregate mixes with the activator to the required placement consistency without water as a diluent. Application and cure temperature is -25 to 45 deg C. ASTM C807 initial set time is 3 to 11 minutes and final set time is 15 to 22 minutes. Compressive strength develops from 17 to 21 N/mm^2 after 2 hours to 48 to 55 N/mm^2 after 28 days.
Key features
- Setting Profile: Initial set time is 3 to 11 minutes by ASTM C807; final set time is 15 to 22 minutes.
- -25 to 45 deg C Placement Range: Application and cure temperature is -25 to 45 deg C.
- Compressive Strength Development: Compressive strength is 17 to 21 N/mm^2 after 2 hours and 48 to 55 N/mm^2 after 28 days.
Applications
Pothole and loading-area repair, concrete floor repair, machinery anchoring, and grouting of bedplates, soleplates, rails, bolts, and related concrete interfaces.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Additional Information
As supplied
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Gray liquid | Mixed to desired consistency | |
| Activator-to-aggregate quantity | 3.8 L to 20.4 kg | Approximate mixing quantity | |
| Application and cure temperature | -25 to 45 | deg C | During placement and cure |
| Initial set time | 3 to 11 | min | ASTM C807 |
| Final set time | 15 to 22 | min | ASTM C807 |
| Coverage | 0.45 | m^2 | At 0.64 cm thickness per 4.54 kg |
Cured material
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Coefficient of thermal expansion | 11x10^-6 | K^-1 | ASTM C531 |
| Compressive strength after 2 hours | 17 to 21 | N/mm^2 | Cured repair material |
| Compressive strength after 3 days | 28 to 41 | N/mm^2 | Cured repair material |
| Compressive strength after 28 days | 48 to 55 | N/mm^2 | Cured repair material |
| Compressive strength after 1 year | 90 | N/mm^2 | Cured repair material |