LORD 506/17
Harmonization Code : 3506.10.00.00 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg
Main features
- 8-12 Minute Handling Strength
- 10:1 Accelerator 17 Volume Mix
- -40 to 149 deg C Temperature Range
Product Description
LORD 506/Accelerator 17 is a two-part, semi-flexible acrylic adhesive system for bonding thermoplastics, thermosets and prepared metals. LORD 506 is a colorless-to-amber liquid with typical viscosity of 20,000-70,000 cP at 25 deg C. With Accelerator 17, the system uses a 10:1 volume ratio, provides a 4-6 minute working time, and reaches handling strength in 8-12 minutes at 24 deg C. Complete cure takes 24 hours at room temperature. The cured system is used from -40 to 149 deg C and accommodates shock and sudden stress loading.
Key features
- System Mixing: LORD 506 and Accelerator 17 use a 10:1 adhesive-to-accelerator ratio by volume.
- Assembly Handling: The mixed system reaches handling strength in 8 to 12 minutes at 24 deg C.
- Semi-Flexible Response: The cured adhesive accommodates shock and sudden stress loading.
Applications
ABS, acrylic, polycarbonate, FRP, prepared metals, urethane, phenolic, polysulfone and vinyl.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Physical Properties
Additional Information
As-supplied / before-processing properties
Component values apply to LORD 506; mix and timing values apply specifically to the LORD 506/Accelerator 17 system.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| LORD 506 viscosity | 20,000-70,000 | cP | Typical; Brookfield HBT, spindle 3, 5 rpm; 25 deg C |
| LORD 506 density | 989-1,036 | kg/m3 | Typical |
| Flash point, closed cup | 11 | deg C | Typical; LORD 506 component |
| Mix ratio | 10:1 | by volume | LORD 506 adhesive to Accelerator 17 |
| Solids content | 100 | % | Typical; mixed system |
| Working time | 4-6 | minutes | Typical; mixed system at 24 deg C |
| Time to handling strength | 8-12 | minutes | Typical; mixed system at 24 deg C; 100 psi endpoint |
| Shelf life | 6 | months | Original unopened container below 27 deg C |